Products >> Paints >> Decorative Paints :

 

 

Super Synthetic Enamels.
Synthetic Enamels.
Cement & Wood Primer White.
Red oxide Primer.
Red oxide  Zinc Chromate Primer.
Under Coating Paints.
Synthetic Clear Varnish.
Acrylic Plastic Emulsion Paints.
Acrylic Distemper.


            Super synthetic enamels, cement and wood primer, red oxide

Marudhar Synthetic Enamel

Marudhar synthetic enamel is a quick drying, high gloss enamel having hard-wearing properties. It is suitable for exterior and interior use, both on wood and metal surface. It conforms to specification IS. 2933 and IS-133 and have following characteristics :-
     

Supply Viscosity - 90-110 Secs. By flow Cup No.4@ 30’C.

Weight Per 10 Litre - 9.0 TO 11.5 Kgs.

Drying Time - Surface Dry within 2 hours
                    - Hard Dry Within 6 Hours.

Color - Close match to standard shade.

Finish - Smooth & Glossy
 

Scratch Hardness - Passes 1500 gms.

Flexibility & Adhesion - Satisfactory

Covering Capacity - 12-14Sq. Meters per Litre.

Exterior Durability - Excellent

Resistance To Water - Satisfactory.

Application - By brush or spray after thinning with Marudhar Synthetic Thinner. The complete system is to apply- One coat Marudhar Red Oxide Zinc. Chromate Primer. One coat Marudhar Surface Grey filler. Wet sanding with Emery Paper. The above dried and smooth surface is finished with two coats of Marudhar Synthetic Enamel.
 

[ Top ]

 

Marudhar Surfacer Grey

Marudhar surfacer Grey is a heavy pigmented composition giving desired filling properties to overcome surface defects and smooth finish. It conforms to specification IS-110-68 and has the following characteristics :-
     
Supply Viscosity - 80 Secs, min By flow Cup No.4@ 30’C

Weight Per 10 Litre - 14.40 lbs. Approx. 15.6 “

Drying Time - Surface Dry within 2 hours
- Hard Dry Within 8 Hours.

Color - Grey

Finish - Smooth & Matt.

Finishing - To be over coated with Marudhar Synthetic Enamel.
Scratch Hardness - Passes 1,000 gms.

Flexibility & Adhesion - Satisfactory

Covering Capacity - About 15 sq. meters per litre.

 Application - It is applied on primed surface, which should be slightly denibbed by fine emery paper No. 320, it is ready for use for application by brush or spray should be thinned with Marudhar Synthetic Thinner
.

Marudhar Synthetic Putty

Marudhar synthetic Putty is applied by special Putty Knife.
 
Consistency - Thick Paste Consistency.

Color - Grey.

Drying Time - 6-8 Hours.

Application - Marudhar Synthetic Putty is applied over Primed surface to cover the Uneven surface. After drying it should be cut with 320 waterproof Abrasive
Paper, before applying surface or finishing enamel.

 


Marudhar Zinc Chromate Primer

MARUDHAR ZINC CHROMATE PRIMER is an extremely good anticorrosive. Primer designed for use both on Ferrous and non-ferrous surfaces such as Aluminium, G.1. Sheets etc. It should be recoated as soon as possible with undercoating or surfacer and / or finishing enamel.3
 

Supply Viscosity - 80 secs by flow Cup No.4@ 30’C

Weight Per 10 Litre
- 13.0 Kgs. Approx

Drying Time - Surface Dry within 2 hours
- Hard Dry Within 4 Hours.

Color - Yellow

Finish - Smooth and Matt.

Scratch Hardness - Passes 1000 gm.

Flexibility & Adhesion - Satisfactory.

Covering Capacity - About 15 Square meters per Litre.

Protection Against - No sign of break down of the paint film or under film corrosion.
Corrosion Under
Conditions Of Condensation
When Tested As Per IS-101
 

Finishing - To be over-coated with Marudhar Surfacer Grey and Marudhar Synthetic Enamel of the desired color. Material conforming to IS-104 can also be supplied.

Resistance To Salt - Satisfactory SPRAY FOR 96 HOURS.

Application :
BY Brush - It is ready for use
By Spray - Thin with Marudhar Synthetic Thinner to application viscosity of 40 secs. by Flow cup No.4 and apply at 40-50 lbs p.s.i. pressure


Surface Preparation - (a) Ferrous surface- should be properly degreased, derusted and sand blasted or phosphate coated before applying this primer.

(b) Aluminium and galvanised surfaces- Degreased and cleaned with clean cloth. It should be preferably first coated with Marudhar Etch Primer followed with Marudhar Zinc Chromate Primer to get best performance.

Marudhar Red Oxide Zinc Chromate Primers

Marudhar Red Oxide Zinc Chromate Primer is an anticorrosive Primer most Suitable for steel surface . It is recommended on any type of Prefabricated Steel Components where protection against corrosion is very much needed such as steel structures, Tractors, heavy vehicles, bridges, storage fuel tanks above and below grounds etc. This quality conforms to Defense specification JSS- 3-47-13 & IS- 2074 and has following characteristics :-
 

Supply Viscosity - 80 secs , min. by flow Cup No.4@ 30’C

Weight Per 10 Litre - 13.8 Kgs. Approx

Drying Time - Surface Dry within 2 hours
-Hard Dry Within 6 Hours.

Color - Red oxide.

Finish - Smooth and Matt.

Scratch Hardness - Passes 1000 gm.

Flexibility & Adhesion - Satisfactory

Covering Capacity - About 20 Square meters per Litre.

Protection Against - No sign of break down of the paint film or under film corrosion.
 

Corrosion Under Conditions
Of Condensation When
Tested As Per IS-101

Resistance To Salt - Satisfactory SPRAY FOR 96 HOURS

Application -
BY Brush - It is ready for use
By Spray - Thin with Marudhar Synthetic Thinner to application viscosity of 40 secs. by Flow cup No.4 and apply at 40-50 lbs p.s.i. pressure
 
Surface Preparation - In order to get good finish and performance of Marudhar Primer, the surface
should be thoroughly cleaned, degreased, derusted and preferably lightly sand blasted before applying the Primer.


Finishing - To be over-coated with Marudhar Surface Grey and Marudhar Synthetic Enamel
of the desired color.



 





Zinc chromate, under coating paits, acrylic distemper